</script>请问各位大侠：检查镀层与基体的附着强度一般用什么方法？
哪些试验室有这些检测项目？
请不齿下教
谢谢hua_tan (2006-4-20 15:05:34)很简单呀.用介刀将镀层切为60个左右的1mmX1mm的小方格,然后用3M胶纸812,粘看是否脱落.yykdmagnet (2006-4-21 08:23:33)楼上的划格法是一个检测方法，另外还有专用的拉拔附着力试验仪，另外跌落试验也是一个检验方式，主要看客户的要求了lwxe (2006-4-21 09:15:00)可用Bend test 或高温法测试， 具体方法如下(摘录)：
The test speciments shall be bent repeatedly through an angle of 180 degree on a diameter equal to the thickness of the specimen until fracture of the basis metal occurs. Following fracture of the basis metal, it shall not be possible to detach any areas of the coatings with a sharp instrument. When the plated articles are not readily adaptable to the bend test, adhesion may be determined on the plated article by cutting the plating from the basis metal at the inte**ce in a continuous path, and examining at four diameters magnification to determine whether removal has been caused by the cutting away of an adherent plate or by the lifting of th nonadherent plate.
Alternate adhesion test.
The test specimens shall be baked at a temperature of 215+/-5 degree C for a period of 30 minutes, to determine adhesion of the plating.jackmayor (2006-4-21 09:41:29)QUOTE:
<blockquote style="border: 1px dotted #DDD; margin: 0 1em 1em; padding: 0.5em; line-height: 1.8em;">原帖由 hua_tan 于 2006-4-20 15:05 发表
很简单呀.用介刀将镀层切为60个左右的1mmX1mm的小方格,然后用3M胶纸812,粘看是否脱落. 是这样的。jshyc (2006-4-21 09:59:54)这个部件很小，而且形状比较特别，划格试验不好做。
高温测试倒是可以试一下，
再有请问一下跌落试验怎么做啊？
谢谢 工业工程的发展离不开这个网站 看了楼主的帖子,不由得精神为之一振,自觉七经八脉为之一畅,七窍倒也开了六巧半,自古英雄出少年,楼主年纪轻轻,就有经天纬地之才,定国安邦之智,古人云,卧龙凤雏得一而安天下,而今,天佑我大中华,沧海桑田5000年,中华神州平地一声雷,飞沙走石,大舞迷天,朦胧中,只见顶天立地一金甲天神立于天地间,这人英雄手持双斧,二目如电,一斧下去,混沌初开,二斧下去,女娲造人,三斧下去,小生倾倒.得此大英雄,实耐之幸也,民之福也,怎不叫人喜极而泣.......古人有少年楼主说为证,少年之楼主如红日初升，其道大光；河出伏流，一泻汪洋；潜龙腾渊，鳞爪飞扬；乳虎啸谷，百兽震惶；鹰隼试翼，风尘吸张；奇花初胎，皇皇；干将发硎，有作其芒；天戴其苍，地履其黄；纵有千古，横有八荒；小生对楼主之仰慕如滔滔江水连绵不绝,海枯石烂,天崩地裂,永不变心. 看帖回帖是美德！:lol 我要拿出这帖子奉献给世人赏阅，我要把这个帖子一直往上顶，往上顶！顶到所有人都看到为止！ 从入职到现在，一直默默的关注 新人求罩 看帖回帖是美德！:lol 潜水党出来挽一个 支持楼主